Two parts silicone sealant Feature:
1, two-component,the curing speed is adjustable,deep curing fast,
suitable for plant construction.
2, Neutral curing, no corrosive with the building materials such as
metal,coated glass.
3, Low molecular alcohols will be released when curing, without
excitant or unpleasant smells.
4, Excellent resistance on weathering, ultraviolet ray, ozone and
water.
5, Outstanding temperature resistant performance, and it will
always keep a good strength and flexibility at -30℃ and
+90℃,neither become brittle ,hardening or cracking at low
temperatures, nor will become soft and degradation at high
temperature
6, Good compatibility with other neutral silicone rubber;
Solidify time
1,8100 mixing proportion is A:B = 9-11:1 (volume) or 14-16:1
(weight), while 10:1(volume) or 14:1(weight) was recommended. The
curing speed can be improved with the increase of the proportion of
component B, but shall not exceed the proportion range,
otherwise it will cause abnormal curing or resulting in a decline
in the performance of the sealant.
2,The colloidal start crosslinking reaction when 8100 mixes in two
components and the surface dry time associated with the mixing
ratio of A and B component.
Main Application:
The second bonded seal of hollow glass;
Package:
1,Large group:Pack 8100A in 200L steel drum(net capacity was
190L),pack 8100B in 20L plastic drum(net capacity was 19L).
2,Small group:Pack 8100A in 20L steel drum(net capacity was
19L),pack 8100B in 2L plastic drum(8 * 300 g/piece).
| sag degree(mm) | gravity standard(23±2℃) dry time(min) | shore hardness (shore A) | applicable period (min) | modulus (Mpa) |
| ≤1 | ≤180 | 20-60 | ≥20 | 0.4-0.6 |